In this study, 5%, 15%, 30%, 45%, 60%, and 75% graphite filled cyclo-olefin copolymer (COC) polymers have been produced by extrusion and pressure molding technics. Wear and friction tests have been carried out at the sliding speeds of 0.5 m/s, 1.0 m/s and 1.5 m/s, applied loads of 20 N, 30 N, 40 N and under dry conditions using pin-on-disc system. As a result of the experiments, coefficient of friction increases while wear rate decreases with increase both applied load and sliding speed. The lowest coefficient of friction and the wear ratio have been obtained in weight of 75% graphite filled COC composites. The coefficient of friction and wear rate of the 75% graphite filled COC polymer decreased by 87.7% and 498.79%, respectively.
Bu çalışmada, ağırlıkça %5, %15, %30, %45, %60 ve %75 oranlarında grafit katkılı siklo-olefin kopolimer (COC) kompozitleri ekstrüzyon ve basınçlı kalıplama yöntemleri ile üretilmiştir. Sürtünme ve aşınma deneyleri, disk üzerinde pim sistemi (pim-disk) ile kuru ortam şartlarında, 20 N, 30 N ve 40 N yük ve 0.5 m/s, 1.0 m/s ve 1.5 m/s kayma hızında gerçekleştirilmiştir. COC polimeri ve grafit katkılı COC kompozitlerin artan kayma hızı ve yüke bağlı olarak sürtünme katsayısı azalmış aşınma oranı ise artmıştır. En düşük sürtünme katsayısı ve aşınma oranı %75 grafit katkılı COC kompozitinde elde edilmiştir. COC polimerine eklenen %75 oranındaki grafit katkısı ile sürtünme katsayısı %87.7 oranında, aşınma oranı ise %498.79 oranında azalmıştır.
Birincil Dil | Türkçe |
---|---|
Konular | Mühendislik |
Bölüm | Araştırma Makalesi |
Yazarlar | |
Yayımlanma Tarihi | 1 Eylül 2021 |
Gönderilme Tarihi | 6 Nisan 2021 |
Kabul Tarihi | 24 Temmuz 2021 |
Yayımlandığı Sayı | Yıl 2021 Cilt: 9 Sayı: 3 |